- 熔體流動速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ExxonMobil Method | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ExxonMobil Method | ||
| 2.6 g/10 min @Load 10.0 kg, Temperature 190 °C | 2.6 g/10 min @Load 22.0 lb, Temperature 374 °F | ExxonMobil Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.9 MPa | 1720 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 13.1 MPa | 1900 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 630 % | 630 % | ASTM D882 | ||
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 | ||
| Puncture Energy | 2.135 J | 1.575 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength MD | 70 g | 70 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 570 g | 570 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 1.38 g/micron | 35.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 11.2 g/micron | 285 g/mil | ASTM D1922 | ||
| Dart Drop | 4.92 g/micron | 125 g/mil | ASTM D1709 | ||
| Dart drop Test | 250 g | 0.551 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 25.7 MPa | 3730 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.6 MPa | 3420 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 325 MPa | 47100 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 406 MPa | 58900 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 128 °C | 263 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 112 °C | 234 °F | ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||