- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ExxonMobil Method | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ExxonMobil Method | ||
| 4.0 g/10 min @Load 10.0 kg, Temperature 190 °C | 4.0 g/10 min @Load 22.0 lb, Temperature 374 °F | ExxonMobil Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.6 MPa | 1680 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 70 g | 70 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 770 g | 770 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 1.38 g/micron | 35.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 15.2 g/micron | 385 g/mil | ASTM D1922 | ||
| Dart Drop | 6.30 g/micron | 160 g/mil | ASTM D1709 | ||
| Dart drop Test | 320 g | 0.706 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 26.8 MPa | 3880 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.1 MPa | 3350 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 325 MPa | 47100 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 387 MPa | 56200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 130 °C | 266 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 105 °C | 221 °F | ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||