- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.28
- 熱變形溫度 [℃]: 68.0
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D4883 | ||
| ESCR 100% Igepal? | 80 hour | 80 hour | ASTM D1693 Condition B | ||
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 | ||
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 | ||
| Elongation at Break | 900 % | 900 % | ASTM D638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 | ||
| Tensile Modulus | 2.07 GPa | 300 ksi | ASTM D638 | ||
| Flexural Modulus | 1.28 GPa | 185 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 | ||
| Tensile Impact Strength | 189 kJ/m2 | 90.0 ft-lb/in2 | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 μm/m-°C @Temperature 20.0 °C | 66.7 μin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 | ||
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.