- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.942
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.896
- 熱變形溫度 [℃]: 67.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in3 | ASTM D4883 | ||
| ESCR 100% Igepal? | 550 hour | 550 hour | ASTM D1693 Condition A | ||
| ESCR 10% Igepal? | 50 hour | 50 hour | ASTM D1693 Condition A | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | 190°C/2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 2.0 in/min; ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | 2.0 in/min; ASTM D638 | ||
| Flexural Modulus | 0.896 GPa | 130 ksi | 1% Secant; ASTM D790 | ||
| Impact Test | 108 J @Thickness 3.17 mm, Temperature -40.0 °C | 80.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 244 J @Thickness 6.35 mm, Temperature 25.0 °C | 180 ft-lb @Thickness 0.250 in, Temperature 77.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 129 °C | 264 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Long Term UV 8 Stabilization | ||||
| Form | 35 US Mesh Powder | ||||