- 缺口沖擊強度: 2.3
- 拉伸強度 [MPa]: 19.3
- 彎曲模量 [MPa]: 600
- 熱變形溫度 [℃]: 142.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | F50; ASTM D1693A | ||
| ESCR 10% Igepal? | >= 1000 hour | >= 1000 hour | F50; ASTM D1693A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | ASTM D638 | ||
| Elongation at Break | 700 % | 700 % | ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | ASTM D638 | ||
| Flexural Modulus, 1% Secant | 600 MPa | 87000 psi | ASTM D790B | ||
| Izod Impact, Notched | 2.30 J/cm @Temperature -40.0 °C | 4.30 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| Impact Test | 100 J @Thickness 3.17 mm, Temperature -40.0 °C | 74.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 249 J @Thickness 6.35 mm, Temperature -40.0 °C | 184 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D638 | ||
| Descriptive Properties | |||||
| Crosslink Potential | 2.5 | ExxonMobil Method | |||