- 熔體流動速率 [g/10min]: 0.47
- 密度 [g/cm3]: 0.963
- 拉伸強度 [MPa]: 31.7
- 彎曲模量 [MPa]: 1.48
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in3 | ASTM D4883 |
| ESCR 100% Igepal? | 10 hour | 10 hour | ASTM D1693 Condition B |
| Melt Flow | 0.47 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.47 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 1.48 GPa | 215 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 |
| Tensile Impact Strength | 137 kJ/m2 | 65.0 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 260 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |