- 熔體流動(dòng)速率 [g/10min]: 0.73
- 密度 [g/cm3]: 0.963
- 拉伸強(qiáng)度 [MPa]: 32.4
- 彎曲模量 [MPa]: 1.72
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in3 | ASTM D4883 |
| ESCR 100% Igepal? | 10 hour | 10 hour | ASTM D1693 Condition B |
| Melt Flow | 0.73 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.73 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.4 MPa | 4700 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 1.72 GPa | 250 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 |
| Tensile Impact Strength | 126 kJ/m2 | 60.0 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 260 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 191 °C | 375 °F | |