- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.949
- 拉伸強度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.24
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D4883 |
| ESCR 100% Igepal? | >= 800 hour | >= 800 hour | ASTM D1693 Condition B |
| Melt Flow | 10 g/10 min | 10 g/10 min | 190 / 21.6 (HLMI); ASTM D1238 |
| <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | <= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 |
| Tensile Impact Strength | 252 kJ/m2 | 120 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 °C | 400 °F | |