- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.946
- 拉伸強度 [MPa]: 24.1
- 彎曲模量 [MPa]: 1.03
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D4883 | ||
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | ASTM D1693 Condition B | ||
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | 190 / 21.6 (HLMI); ASTM D1238 | ||
| <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | <= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 | ||
| Elongation at Break | 1100 % | 1100 % | ASTM D638 | ||
| Flexural Modulus | 1.03 GPa | 150 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 | ||
| Tensile Impact Strength | 420 kJ/m2 | 200 ft-lb/in2 | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 127 °C | 260 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 204 °C | 400 °F | |||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||