- 熔體流動速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.952
- 缺口沖擊強度: 0.587
- 拉伸強度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.17
- 熱變形溫度 [℃]: 66.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 6.0 hour | 6.0 hour | Cond. B, 10%; ASTM D1693 | ||
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 26.20 MPa | 3800 psi | ASTM D638 | ||
| Elongation at Break | 1200 % | 1200 % | ASTM D638 | ||
| Flexural Modulus | 1.17 GPa | 170 ksi | 2% Secant; ASTM D790 | ||
| Flexural Modulus, 1% Secant | 1310 MPa | 190000 psi | ASTM D790 | ||
| Izod Impact, Notched | 0.587 J/cm @Temperature -40.0 °C | 1.10 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 132 °C | 270 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.6 °C | 152 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 39.0 °C | 102 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Standard Processing Antioxidants Stabilizer | ||||
| Form | Pellet | ||||