- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.952
- 彎曲模量 [MPa]: 1.24
- 熱變形溫度 [℃]: 73.9
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | ASTM D2561 |
| ESCR 100% Igepal? | 25.0 hour | 25.0 hour | ASTM D1693 |
| Melt Flow | 0.350 g/10 min | 0.350 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66.0 | 66.0 | ASTM D2240 |
| Tensile Strength at Break | 26.9 MPa | 3900 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
| Tensile Impact | 61.4 J/cm | 115 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | F50; ASTM D746 |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |