- 熔體流動速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.96
- 缺口沖擊強度: 0.395
- 彎曲模量 [MPa]: 1.118
- 熱變形溫度 [℃]: 74.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in3 | ASTM D1895 |
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM D1505 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 190 °C | 18 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 28.2 cm | 11.1 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 29.6 MPa | 4300 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.8680 GPa | 125.9 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 1.001 GPa | 145.2 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 1.118 GPa | 162.2 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 1.369 GPa | 198.5 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.474 GPa | 213.8 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.395 J/cm | 0.740 ft-lb/in | ASTM D256 |
| 5.34 J/cm @Temperature -18.0 °C | 10.0 ft-lb/in @Temperature -0.400 °F | ASTM D4812 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 133.0 °C | 271.4 °F | ASTM D3418 |
| Crystallization Temperature | 115.7 °C | 240.3 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |