- 熔體流動速率 [g/10min]: 0.33
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Water Vapor Transmission | 3.30 g/m2/day | 0.213 g/100 in2/day | ASTM F372 |
| Oxygen Transmission Rate | 2400 cc/m2/day | 155 cc/100 in2/day | ASTM D3985 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.33 g/10 min | 0.33 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 24.8 MPa | 3600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 28.3 MPa | 4100 psi | ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 |
| Elmendorf Tear Strength MD | 31 g | 31 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1200 g | 1200 g | ASTM D1922 |
| Dart Drop | 1.38 g/micron | 35.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 43.4 MPa | 6300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 758 MPa | 110000 psi | ASTM E111 |
| 1% Secant Modulus, TD | 924 MPa | 134000 psi | ASTM E111 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | |
| Die Opening | 0.1524 cm | 0.06000 in | |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |