- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 25.5 MPa | 3700 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 31.7 MPa | 4600 psi | ASTM D882 |
| Film Elongation at Break, MD | 850 % | 850 % | ASTM D882 |
| Film Elongation at Break, TD | 350 % | 350 % | ASTM D882 |
| Secant Modulus, MD | 0.932 GPa | 135 ksi | ASTM D882 |
| Secant Modulus, TD | 1.07 GPa | 155 ksi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 60.0 °C | 140 °F | Chill Roll |
| Melt Temperature | 177 °C | 350 °F | |