- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.943
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in3 | ASTM D1505 |
| Oxidative Induction Time (OIT) | >= 10 min | >= 10 min | ASTM D3985 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| 1% Secant Modulus | 758 MPa | 110000 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |