- 熔體流動(dòng)速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.954
- 拉伸強(qiáng)度 [MPa]: 28.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2"/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | 2"/min; ASTM D638 |
| Tensile Modulus | 1.34 GPa | 195 ksi | 1% Secant; 0.5"/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 56.7 °C | 134 °F | ASTM D3418 |
| Vicat Softening Point | 80.0 °C | 176 °F | B/50 K/h 10N; ASTM D1525 |
| 130 °C | 266 °F | A/50 K/h 10N; ASTM D1525 | |