- 熔體流動速率 [g/10min]: 0.17
- 密度 [g/cm3]: 0.94
- 拉伸強度 [MPa]: 21.9
- 熱變形溫度 [℃]: 64.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Water Vapor Transmission | 5.10 g/m2/day | 0.328 g/100 in2/day | ASTM F372 |
| Oxygen Transmission Rate | 2450 cc/m2/day | 158 cc/100 in2/day | ASTM D3965 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | molding; ASTM D1693 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.17 g/10 min | 0.17 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | molding; ASTM D2240 |
| Film Tensile Strength at Yield, MD | 19.3 MPa | 2800 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 228 MPa | 33000 psi | ASTM D882 |
| Tensile Strength, Yield | 21.9 MPa | 3180 psi | molding; ASTM D638 |
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 |
| Elmendorf Tear Strength MD | 40 g | 40 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1150 g | 1150 g | ASTM D1922 |
| Dart Drop | 1.38 g/micron | 35.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 46.9 MPa | 6800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.6 MPa | 4300 psi | ASTM D882 |
| 1% Secant Modulus, MD | 565 MPa | 82000 psi | ASTM E111 |
| 1% Secant Modulus, TD | 758 MPa | 110000 psi | ASTM E111 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | molding; ASTM D648 |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | molding; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 221 °C | 410 - 430 °F | |
| Die Opening | 0.1524 cm | 0.06000 in | |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |