- 熔體流動速率 [g/10min]: 62.0
- 密度 [g/cm3]: 0.942
- 缺口沖擊強度: 0.299
- 彎曲模量 [MPa]: 0.9708
- 熱變形溫度 [℃]: 62.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in3 | ASTM D1895 |
| Density | 0.942 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Melt Flow | 62.0 g/10 min @Load 0.980 kg, Temperature 190 °C | 62.0 g/10 min @Load 2.16 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 47.5 cm | 18.7 in | Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67.0 | 67.0 | ASTM D2240 |
| Tensile Strength at Break | 18.5 MPa | 2690 psi | 50 mm/min, Type IV; ASTM D4796 |
| Elongation at Break | 5.00 % | 5.00 % | 50 mm/min, Type IV; ASTM D638 |
| Tensile Modulus | 0.7977 GPa | 115.7 ksi | 1% Secant, 50mm/min; ASTM D638 |
| 1.008 GPa | 146.2 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 0.9708 GPa | 140.8 ksi | ASTM D790 |
| 1% Secant Modulus | 840.5 MPa | 121900 psi | 12.5mm/min; ASTM D790 |
| 2% Secant Modulus | 0.9018 GPa | 130.8 ksi | 12.5mm/min; ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm @Temperature 23.0 °C | 0.560 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125.4 °C | 257.7 °F | ASTM D3418 |
| Crystallization Temperature | 112.5 °C | 234.5 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.2 °C | 144 °F | ASTM D648 |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |