- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.948
- 拉伸強度 [MPa]: 20.7
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| Melt Flow | 0.800 g/10 min | 0.800 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 24.8 MPa | 3600 psi | ASTM D638 |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+20 ohm-cm | 1.00e+20 ohm-cm | ASTM D991 |
| Dielectric Constant | 2.35 @Frequency 1.00e+6 Hz | 2.35 @Frequency 1.00e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.000260 @Frequency 1.00e+6 Hz | 0.000260 @Frequency 1.00e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 149 - 163 °C | 300 - 325 °F | |
| Zone 2 | 177 - 204 °C | 350 - 400 °F | |
| Zone 3 | 204 - 213 °C | 400 - 415 °F | |
| Zone 4-x | 210 - 216 °C | 410 - 420 °F | |
| Adapter Temperature | 210 - 216 °C | 410 - 420 °F | |
| Die Temperature | 210 - 216 °C | 410 - 420 °F | |
| Melt Temperature | 210 - 216 °C | 410 - 420 °F | |