- 熔體流動速率 [g/10min]: 34.0
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 27.4
- 熱變形溫度 [℃]: 74.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 34 g/10 min | 34 g/10 min | ASTM D1238 |
| Spiral Flow | 39.4 cm | 15.5 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 26.3 MPa | 3820 psi | ASTM D638 |
| Tensile Strength, Yield | 27.4 MPa | 3980 psi | Crosshead speed - 2"min.; ASTM D638 |
| Elongation at Yield | 7.7 % | 7.7 % | Crosshead speed - 2"min.; ASTM D638 |
| 1% Secant Modulus | 1170 MPa | 169000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 0.972 GPa | 141 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |