- 熔體流動速率 [g/10min]: 57.0
- 密度 [g/cm3]: 0.948
- 拉伸強(qiáng)度 [MPa]: 21.4
- 熱變形溫度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| Melt Flow | 57 g/10 min | 57 g/10 min | ASTM D1238 |
| Spiral Flow | 53.8 cm | 21.2 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 25.4 MPa | 3690 psi | ASTM D638 |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | Crosshead speed - 2"min.; ASTM D638 |
| Elongation at Yield | 9.5 % | 9.5 % | Crosshead speed - 2" min; ASTM D638 |
| 1% Secant Modulus | 979 MPa | 142000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 0.827 GPa | 120 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |