- 熔體流動速率 [g/10min]: 0.027
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Thickness | 12.7 microns | 0.500 mil | 4:1 BUR; Neck Height = 8 Die Diameters |
| Melt Flow | 0.027 g/10 min | 0.027 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 41.0 MPa | 5940 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 33.5 MPa | 4860 psi | ASTM D882 |
| Film Elongation at Break, MD | 390 % | 390 % | ASTM D882 |
| Film Elongation at Break, TD | 260 % | 260 % | ASTM D882 |
| Dart Drop, Total Energy | 2.44 J | 1.80 ft-lb | ASTM D3420 |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 18 g | 18 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 65.1 MPa | 9440 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 66.7 MPa | 9680 psi | ASTM D882 |
| 1% Secant Modulus, MD | 1150 MPa | 167000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 979 MPa | 142000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | |