- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 28.3
- 彎曲模量 [MPa]: 1.23
- 熱變形溫度 [℃]: 76.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.23 GPa | 178 ksi | ASTM D790 |
| Tensile Impact | 86.0 J/cm | 161 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |