- 熔體流動速率 [g/10min]: 81.0
- 密度 [g/cm3]: 0.953
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.610 g/cc | 0.0220 lb/in3 | |
| Melt Flow | 81 g/10 min @Load 2.16 kg, Temperature 190 °C | 81 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 40.6 cm | 16.0 in | NOVA Snake Flow Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 260 °C | 338 - 500 °F | |