- 熔體流動(dòng)速率 [g/10min]: 0.41
- 密度 [g/cm3]: 0.957
- 拉伸強(qiáng)度 [MPa]: 31.0
- 彎曲模量 [MPa]: 1.21
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | 100 hour | 100 hour | F50, Condition A, ASTM D1693 |
| Melt Flow | 0.41 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.41 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | at 500 mm/min; ASTM D638 |
| 860 % | 860 % | at 50 mm/min; ASTM D638 | |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 205 °C | 320 - 401 °F | |