- 熔體流動速率 [g/10min]: 0.38
- 密度 [g/cm3]: 0.946
- 拉伸強度 [MPa]: 21.0
- 彎曲強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 0.500
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in3 | |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F0, ASTM D1693 |
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.38 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 950 % | 950 % | ASTM D638 |
| Flexural Modulus | 0.500 GPa | 72.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 200 °C | 392 °F | |