- 熔體流動速率 [g/10min]: 57.0
- 密度 [g/cm3]: 0.949
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.965
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.610 g/cc | 0.0220 lb/in3 | |
| Melt Flow | 57 g/10 min @Load 2.16 kg, Temperature 190 °C | 57 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 38.0 cm | 15.0 in | NOVA Snake Flow Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 260 °C | 338 - 500 °F | |