- 熔體流動速率 [g/10min]: 0.19
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.03
- 熱變形溫度 [℃]: 67.0
- 脆化溫度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 0.19 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.19 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 149 ksi | 1% Secant; ASTM D 790 |
| Tensile Impact Strength | 120 kJ/m2 | 57.1 ft-lb/in2 | S bar; ASTM D 1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D746 |