- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 1.28
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 1000 hour | 1000 hour | Condition A, F50, Condition B: 1000; ASTM D1693 |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in per min; ASTM D638, Type IV |
| Elongation at Break | 600 % | 600 % | 2 in per min; ASTM D638, Type IV |
| Flexural Modulus | 1.28 GPa | 186 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |