- 熔體流動速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.955
- 拉伸強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 1.378
- 脆化溫度 [℃]: -180.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 80 hour | 80 hour | Condition A, F50, ASTM D1693; Bottle ESCR: 250, ASTM D2561 |
| Melt Flow | 21 g/10 min | 21 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.378 GPa | 199.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -180 °C | <= -292 °F | ASTM D746 |