- 密度 [g/cm3]: 0.95
- 拉伸強(qiáng)度 [MPa]: 25.0
- 彎曲模量 [MPa]: 1.172
- 脆化溫度 [℃]: -91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 600 hour @Temperature 50.0 °C | >= 600 hour @Temperature 122 °F | Condition A and Condition B; ASTM D 1693 |
| High Load Melt Index | 8.3 g/10 min @Load 21.6 kg, Temperature 190 °C | 8.3 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 Type IV |
| Flexural Modulus | 1.172 GPa | 170.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -91.0 °C | <= -132 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 154 - 182 °C | 309 - 360 °F | Thermoforming Surface |
| 188 - 232 °C | 370 - 450 °F | Blow Molding | |
| 232 - 268 °C | 450 - 514 °F | Extrusion | |