- 密度 [g/cm3]: 0.941
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.690
- 脆化溫度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | Condition A; ASTM D 1693 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 Type IV |
| Elongation at Break | 450 % | 450 % | ASTM D638 Type IV |
| Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 246 - 326 °C | 475 - 619 °F | oven temperature for hot air machines 246-326°C, marlex crosslinkable resins require special handling during processing |