- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.952
- 拉伸強(qiáng)度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.309
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | Condition B, F50 |
| ESCR 100% Igepal? | 50 hour | 50 hour | Condition A, F50 CO-630; ASTM D1693 |
| ESCR, Bottle | 250 hour @Temperature 60.0 °C | 250 hour @Temperature 140 °F | F50 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 2 in per min; ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.309 GPa | 189.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 182 °C | 340 - 360 °F | Thermoforming Surface |
| 171 - 204 °C | 340 - 399 °F | Blow Molding | |
| 194 - 216 °C | 381 - 421 °F | Extrusion | |