- 熔體流動(dòng)速率 [g/10min]: 62.0
- 密度 [g/cm3]: 0.953
- 拉伸強(qiáng)度 [MPa]: 22.8
- 彎曲模量 [MPa]: 0.830
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 62 g/10 min @Load 2.16 kg, Temperature 190 °C | 62 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 1612 g/10 min @Load 21.6 kg, Temperature 190 °C | 1612 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.8 MPa | 3310 psi | ASTM D638 |
| Elongation at Break | <= 100 % | <= 100 % | ASTM D638 |
| Flexural Modulus | 0.830 GPa | 120 ksi | 3 pt. secant; ASTM D790 |
| 1.21 GPa | 175 ksi | 3 pt. Tangent; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525 |