- 熔體流動速率 [g/10min]: 55.0
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 55 g/10 min @Load 2.16 kg, Temperature 190 °C | 55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 1430 g/10 min @Load 21.6 kg, Temperature 190 °C | 1430 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | <= 100 % | <= 100 % | ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | 3 pt. secant. ASTM D790 |
| Tensile Impact Strength | 34.0 kJ/m2 | 16.2 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |