- 熔體流動速率 [g/10min]: 40.0
- 拉伸強度 [MPa]: 24.0
- 彎曲模量 [MPa]: 0.979
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.952 g/cc | 0.952 g/cc | ASTM D1505 |
| ESCR 100% Igepal? | <= 10 hour | <= 10 hour | Condition B, F50; ASTM D1693 |
| Melt Flow | 40 g/10 min @Load 2.16 kg, Temperature 190 °C | 40 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | <= 100 % | <= 100 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 0.979 GPa | 142 ksi | Tangent; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, Type I Specimen; ASTM D746 |