- 密度 [g/cm3]: 0.951
- 拉伸強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 1.31
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 50 hour | 50 hour | Conditions A and B; ASTM D1693 |
| Melt Index of Compound | 0.35 g/10 min | 0.35 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 600 % | 600 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, type 1 specimen; ASTM D746 |