- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 1.31
- 熱變形溫度 [℃]: 74.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | Conditions A and B; ASTM D1693 |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | Condition 190/2.16, HLMI; ASTM D1505 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 800 % | 800 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Tensile Impact Strength | 450 kJ/m2 | 214 ft-lb/in2 | Type S bar; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | Method A; ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | Loading 1, Rate A; ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, type 1 specimen; ASTM D746 |