- 熔體流動速率 [g/10min]: 5.5
- 拉伸強度 [MPa]: 24.0
- 彎曲模量 [MPa]: 1.07
- 熱變形溫度 [℃]: 66.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.945 g/cc | 0.945 g/cc | ASTM D1505 |
| ESCR 100% Igepal? | >= 2000 hour | >= 2000 hour | Condition A, F50; ASTM D1693 |
| >= 2000 hour | >= 2000 hour | Condition B, F50; ASTM D1693 | |
| Melt Flow | 5.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 5.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 700 % | 700 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | Tangent; ASTM D790 |
| Tensile Impact Strength | 580 kJ/m2 | 276 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, Type I Specimen; ASTM D746 |