- 熔體流動(dòng)速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.951
- 拉伸強(qiáng)度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.930
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in3 | ASTM-D792 |
| Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in3 | ASTM-D1895 |
| Particle Size | 170 μm | 170 μm | Average, Dp50; ASTM-D1921 |
| Viscosity Test | 470 cm3/g | 470 cm3/g | Intrinsic; ASTM-D4020 |
| Molecular Weight | 550000 g/mol | 550000 g/mol | |
| Melt Flow | 0.70 g/10 min @Load 21.6 kg, Temperature 190 °C | 0.70 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | 15 sec; ASTM-D2240 |
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | ASTM-D638 / ISO 527 |
| Tensile Strength, Yield | >= 20.0 MPa | >= 2900 psi | ASTM-D638 / ISO 527 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM-D638 / ISO 527 |
| Flexural Modulus | 0.930 GPa | 135 ksi | ASTM-D790 |
| Charpy Impact, Notched | >= 5.00 J/cm2 | >= 23.8 ft-lb/in2 | double-notched specimens (14° v-notch on both sides); ISO 11542-2 |
| Sand Slurry | 80 | 80 | Sand slurry - Internal, reference PE500 = 100 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 80.0 °C @Load 5.10 kg | 176 °F @Load 11.2 lb | ASTM-D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 136 °C | 277 °F | ASTM-D3418 |