- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.955
- 缺口沖擊強度: 3.45
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1320
- 熱變形溫度 [℃]: 74.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM-D792 |
| ESCR 100% Igepal? | 530 hour @Thickness 2.00 mm, Temperature 50.0 °C | 530 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Oxidative Induction Time (OIT) | >= 40 min @Temperature 200 °C | >= 40 min @Temperature 392 °F | ASTM-D3895 |
| Melt Flow | 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 8.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM-D2240 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM-D638 |
| Elongation at Break | 850 % | 850 % | ASTM-D638 |
| Elongation at Yield | 8.2 % | 8.2 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1320 MPa | 191000 psi | ASTM-D790 |
| Izod Impact, Notched | 3.45 J/cm | 6.46 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM-D648 |
| Vicat Softening Point | 128 °C @Load 1.02 kg | 262 °F @Load 2.25 lb | ASTM-D1525 |