- 熔體流動速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.957
- 缺口沖擊強度: 0.85
- 拉伸強度 [MPa]: 23.0
- 彎曲模量 [MPa]: 980
- 熱變形溫度 [℃]: 68.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in3 | ASTM-D792 | ||
| ESCR 100% Igepal? | >= 1000 hour @Thickness 2.00 mm, Temperature 50.0 °C | >= 1000 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 | ||
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | ASTM-D2240 | ||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM-D638 | ||
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM-D638 | ||
| Elongation at Break | 840 % | 840 % | ASTM-D638 | ||
| Elongation at Yield | 9.9 % | 9.9 % | ASTM-D638 | ||
| Flexural Modulus, 1% Secant | 980 MPa | 142000 psi | ASTM-D790 | ||
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM-D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 | ||
| Vicat Softening Point | 121 °C @Load 1.02 kg | 250 °F @Load 2.25 lb | ASTM-D1525 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Carbon, C | 2.4 % | 2.4 % | Black Content; ASTM-D1603 | ||
| Descriptive Properties | |||||
| UV Absorption Coefficient (Abs/cm) | > 3000 | ASTM-D3349 | |||