- 熔體流動速率 [g/10min]: 4.5
- 缺口沖擊強度: 0.45
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1270
- 熱變形溫度 [℃]: 74.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.954 g/cc | 0.954 g/cc | ASTM D792 |
| ESCR 100% Igepal? | <= 5.0 hour @Temperature 50.0 °C | <= 5.0 hour @Temperature 122 °F | h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Flexural Modulus, 1% Secant | 1270 MPa | 184000 psi | ASTM D790 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |