- 熔體流動(dòng)速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.80 MPa | 1280 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.70 MPa | 1260 psi | ASTM D882 |
| Film Elongation at Break, MD | 475 % | 475 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Secant Modulus, MD | 0.175 GPa | 25.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.189 GPa | 27.4 ksi | ASTM D882 |
| Coefficient of Friction | 0.51 | 0.51 | ASTM D1894 |
| Elmendorf Tear Strength MD | 165 g | 165 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 335 g | 335 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.11 g/micron | 206 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.5 g/micron | 419 g/mil | ASTM D1922 |
| Dart Drop | >= 49.2 g/micron | >= 1250 g/mil | F50; ASTM D1709 |
| Dart drop Test | >= 1000 g | >= 2.20 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 72.0 MPa | 10400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 57.0 MPa | 8270 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 118 °C | 244 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 15.1 % | 15.1 % | ASTM D1003 |
| Gloss | 44 % | 44 % | 45°, ASTM D-2457 |