- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.927
- 拉伸強度 [MPa]: 15.2
- 彎曲模量 [MPa]: 0.414
- 熱變形溫度 [℃]: 46.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 16 hour | 16 hour | ASTM D1693 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Tensile Modulus | 0.434 GPa | 63.0 ksi | 1% Secant; ASTM D638 |
| Flexural Modulus | 0.414 GPa | 60.0 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |