- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.919
- 拉伸強度 [MPa]: 10.8
- 彎曲模量 [MPa]: 0.241
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength at Break | 12.2 MPa | 1770 psi | ASTM D638 |
| Tensile Strength, Yield | 10.8 MPa | 1560 psi | ASTM D638 |
| Elongation at Break | 670 % | 670 % | ASTM D638 |
| Tensile Modulus | 0.254 GPa | 36.9 ksi | 1% Secant; ASTM D638 |
| Flexural Modulus | 0.241 GPa | 35.0 ksi | 1% Secant; ASTM D790 |
| Dart Drop | 2.36 g/micron | 60.0 g/mil | ASTM D1709 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 11 % | <= 11 % | ASTM D1003 |
| Gloss | >= 20 % | >= 20 % | 20°; ASTM D2457 |
| 75 % | 75 % | Gardner, 60°; ASTM D523 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 °C | 356 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |