- 熔體流動速率 [g/10min]: 0.18
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 9.65
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 168 hour | 168 hour | no failures; molding; ASTM D1693 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.18 g/10 min | 0.18 g/10 min | ASTM D1238 |
| Antiblock Level | 0.000 ppm | 0.000 ppm | |
| Slip Level | 0.000 ppm | 0.000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42 | 42 | molding; ASTM D2240 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | molding; ASTM D638 |
| Tensile Strength, Yield | 9.65 MPa | 1400 psi | molding; ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 |
| Elongation at Break | 750 % | 750 % | molding; ASTM D638 |
| Elongation at Yield | 100 % | 100 % | molding; ASTM D638 |
| Dart Drop | 4.33 g/micron | 110 g/mil | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.7 MPa | 3000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | F50; molding; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 °C | 430 °F | |
| Die Opening | 0.0635 cm | 0.0250 in | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |