- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ExxonMobil Method | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.4 MPa | 1650 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.8 MPa | 1710 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 230 % | 230 % | ASTM D882 | ||
| Film Elongation at Break, TD | 630 % | 630 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.0 % | 6.0 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.1 % | 5.1 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 430 g | 430 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 8.46 g/micron | 215 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.95 g/micron | 75.0 g/mil | ASTM D1922 | ||
| Dart Drop | 3.35 g/micron | 85.0 g/mil | ASTM D1709 | ||
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.9 MPa | 4040 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 27.1 MPa | 3930 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 232 MPa | 33700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1.97 MPa | 286 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 112 °C | 234 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 99.0 °C | 210 °F | ExxonMobil Method | ||
| Vicat Softening Point | 97.2 °C | 207 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D1003 | ||
| Gloss | 65 % | 65 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.