- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 360 g | 360 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 | ||
| Dart drop Test | 90.0 g | 0.198 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.4 MPa | 3400 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 179 MPa | 26000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 207 MPa | 30000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.0 % | 5.0 % | ASTM D1003 | ||
| Gloss | 70 % | 70 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Antiblock | None | ||||
| Slip | None | ||||