- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ASTM D1505 | ||
| Vinyl Acetate Content | 4.5 % | 4.5 % | |||
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 250 g | 250 g | ASTM D1922 | ||
| Dart drop Test | 320 g | 0.706 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.1 MPa | 3200 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 131 MPa | 19000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 159 MPa | 23000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | |||
| Descriptive Properties | |||||
| Antiblock | High | ||||
| Slip | None | ||||